Liquid Silicone Manufacture

Quantity:
Availability:





Inquire Add to Basket

Material:
Organic Silicone
Application:
Industrial
Certification:
RoHS, MSDS SGS
Uses:
Webbing Coated
Transport Package:
1kg Pot, 5kg and 10kg Plastic Brum, 25kg Iron Drum
Specification:
1kg pot, 5kg and 10kg plastic brum, 25kg iron drum

Silicone Textile Silk Liquid Silicone Manufacture

Products

Product Description

RTV Silicone Rubber Silicone Label Liquid Silicone liquid Silicone for Image Star Silicone Inkjet Ink Screen Printing Ink Label Logo Silicone Textile Ink Features&Usage

Silicone Rubber For Textile THS-1300H

Features & Usage:
THS-1300H is an additional liquid silicone rubber with two components. It showed up good characteristics, such as excellent weatherability, dimensional stability, high transparency, avirulent environmental protection, high-adhesive strength, heatproof temperature exceeds 250C. It is widely used in printing of textile.
Technical parameters:

Items		Data
Before curing	appearance(silicone/curing)	subtransparent/colorless viscous liquid
Before curing	viscosity(silicone/curing)/mPa.s	70000/3000
Operation time(25ºC)/min		90
After curing	hardness/Shore A	42
	density/g.cm^-3	1.10
	Tensile strength/MPa	5.0
	elongation/%	260
	Tear strength/kN.m^-1	15
	Shrinkage/%	0.1

Use method:
1.Mixture: Mix up silicone TCS-1310H with curing agent according ratio 10:1. (If curing agent increased, the curing speed will get slower). Mixture can complete by hand or by equipment.
2.Defoaming: Silicone mixture should be defoaming before printing on textile, the silicone volume will enlarge 1-5 times in vacuum. Please prepare 5times large vessel for defoaming. The mixtures will recover after a few minutes when stop defoaming, The defoaming has completed if no bulb comes out.
3.Moulding: The mixture will inject into mould use squeegee or dispensing process, then heating forming.

Package, storage & Notes:

Silicone package: 20KG/pail. Curing gent: 2KG/tin
Keep it dry, ventilative and cool. To prevent the rain, sun exposure.
Avoid mixing curing agent of condensation silicone. Below also can influent curing effect, such as amine, sulfur compounds, phosphorus compound & melt salt. Avoiding moisture intrusion in using.
The products storage period about 1 year. Its fluidity can be recovered when intense agitation. We advised stir the silicone first then stir the silicone & curing agent mixture second. Expired products also can be used if passed re-inspection.

This products is a non-dangerous goods.

Lead Time :

Quantity(Kilograms)	1 - 200	>200
Est. Time(days)	3	To be negotiated

useing process

webbing printing process

1.mixing the tackifier and its catalyst according the ration 10:1 . printing it on the fabric for the underbase . dry it . the temperature is 80-120 degree.
2. Take out 1310H with the curing agent 1310H mix proportion according to 10:1 fusion, if you want to have a color will need to join at this time is the amount of silica gel 5% of ordinary color paste, if is fluorescent color needs to be added to the 8% of the amount of silica gel. Then stir well. If you want the silica gel to dry more slowly than normal, you need more curing agent. If you want the silica gel to dry faster, the ratio between the gel and curing agent should be controlled at 10:0.8
3 Out of 80 to 100 to screen, a mixture of the silicone and curing agent with scraper scraping back and forth on the screen, you can see silicone has appeared on the fabric, and then use baking dryer running back and forth once. The temperature control is around 120.

4.Use the squeegee to scrape the glue back and forth for a second time, dry it, print it again for a third time, and dry it until it accumulates to the required height. Generally, repeat it for four times.OR THREE time .It depend on you .

PRODUCT EFFECT PHOTO

Certificate

transportation and packaing

• The base rubber in this series is packed in 20kg / per iron can.
• This series of products should be stored in a dry, ventilated and cool place to prevent rain and sunlight.
• Avoid contact with condensation type silicone rubber curing agents during operation. Also likely to cause the compound to not solidify are amines, sulfur and phosphorus compounds, and some metal salts. Avoid moisture ingress during use.
• The storage period of this series of products is one year, and the fluidity can be restored under the action of shearing force (strong stirring). It is recommended that the rubber material be stirred in a container first, and then added with a curing agent and stirred evenly. It can still be used after passing the retest.

Lead Time :

Quantity(Kilograms)	1 - 200	>200
Est. Time(days)	3	To be negotiated

About us
When I choose a product,I want to know the manufacturer of the product to verify that my product is of high quality.So I also prepared our information for you, so you can choose us with confidence.

company information

Dongguan Tianhui New Materials Co., Ltd. ,established in 2011, is a manufacturing enterprise focus on research & development, production, sales and technical services in the liquid silicone industry, covers an area of more than 2000 square meters, located in Wanjiang District, Dongguan city Guangdong Province, near Guangzhou and Shenzhen.
The company mainly deals in liquid silicone ink products: screen printing silicone, concave convex embossed printing silicone, clothing label special silicone rubber, silicone coated webbing, general-purpose silicon rubber mold, rapid prototyping, mold silicone rubber, glossy silicone, matte silicone and molding silicone , thinners and other liquid silicone rubber.
Owe to the advanced production equipment, high-quality raw material suppliers, high-end testing laboratories, professional high-quality production team, our company won the trust of brand customers from domestic and overseas with high quality and good price .
We always perform perfect quality management system and perfect production management system on the base of market-oriented and technical development-oriented,for this reason,our goods quality and sales are always in the leading potion in the market.Also,our boss is a senior engineer whom have more than 20 years experience in liquid silicone industry.
We are dedicated to the development and promotion of environmental - friendly silicone materials.Our products have passed Oeko-tex, ROHS and SGS testing.Quality is the basis of our development, innovation is our driving force, customer satisfaction is our unremitting pursuit!

our boss and our laboratory

our office

our warehouse

our coustomer

Main product
In addition to the main products, our materials can also be used as raw materials for many products, such as cables, cosmetic molds, mechanical supplies, waterproof supplies.